Influence of the use of remineralizing agents on the tensile bond strength of orthodontic brackets

Scientific Reports volume 13, Article number: 507 (2023) Cite this article

831 Accesses

1 Citations

Metrics details

This study aimed to evaluate the influence of the use of remineralizing agents on the tensile bond strength. The study sample consisted of 80 recently extracted molars, which were randomly divided into four experimental groups (n = 20): groups FG1 and FG30, in which fluoride varnish was used, and groups RG1 and RG30, in which Recaldent tooth mousse was used. The mesiobuccal surfaces served as experimental, and distobuccal as control (n = 80). Brackets were bonded to both surfaces and were submitted to a tension test at different time intervals (T1 and T30). Tensile bond strength (TBS) and the amount of adhesive remnant (ARI) were assessed. A statistically significantly lower mean of TBS compared to the control group was found only in the FG1 group (p < 0.001), and no significant difference was found between the other groups. The FG1 group showed significantly higher ARI scores (p < 0.001) compared to the control group. No significant difference was found between the other groups. In conclusion, bonding brackets one day after applying fluoride varnish significantly reduced the TBS, but after 30 days it was set back to an optimal value. The use of Recaldent before orthodontic treatment had no adverse effect.

Dental caries is one of the most common diseases in modern society, and the prevalence of it reaches about 44% of the world's population1. Despite considerable efforts by both dentists and other health professionals to reduce the incidence of caries, the prevalence has decreased by only 4% in the last thirty years2. For this reason, there is now an increasing focus on the prevention of tooth decay, which includes not only dietary correction, personal oral hygiene or the use of prebiotics and probiotics1, but also the use of substances such as fluoride and calcium phosphopeptide—amorphous calcium phosphate (CPP-ACP), a milk-derived protein which is gaining its popularity these days3. These substances can be applied professionally or used by the patients themselves4, 5.

This CPP-ACP delivers bioavailable calcium and phosphate ions and acts as a reservoir for these ions6. Acids release calcium and phosphate ions, which saturate the saliva and then deposit as a calcium phosphate compound on the exposed surface of the tooth7. CPP-ACP is thought to contribute to deeper ion penetration and thus remineralize not only the superficial enamel layer but also the deeper layers of hard tissue of the tooth, which may also improve the aesthetic appearance8, 9. This complex has antimicrobial properties in part because, by bounding to the dental pellicle, it inhibits the adhesion of Streptococcus mutants, highly cariogenic bacteria, to the tooth surface10, 11.

It is common knowledge that fluoride therapy reduces enamel demineralization and increases its resistance to organic acids12. Fluoride has a facilitating effect on the diffusion of calcium and phosphate ions into the demineralized surface. Thus, it can restore the crystalline enamel structure composed of fluorinated hydroxyapatites and fluorapatites, which are more resistant to acids than the primary crystals13.

It is worth noting that dental and occlusal anomalies are also common today. The prevalence varies from 29.2 to 93% of the world’s population14, 15, and the figure is as high as 71% among Europeans16. Due to the high prevalence of such anomalies and the improving economic conditions in both developing and developed countries, people are increasingly focusing on the aesthetics of a smile, leading to an increasing number of patients seeking beautiful smiles through orthodontic treatment17.

Fixed orthodontic appliances—braces—are most often used for the treatment of dental and occlusal anomalies. It is suggested that a minimum tensile bonding strength of 5.9–8 MPa between orthodontic brackets and teeth would be adequate for clinical orthodontic tooth movement18. The tensile bond strength of the brackets depends on many factors, such as the structure of the tooth, the etching time and the acid used, the type of bracket system, the type of bracket, or even previously done procedures on the teeth, such as teeth whitening with 35% hydrogen peroxide19,20,21,22. There is a significant influence on the structure of tooth enamel, as studies have shown that demineralized or fluorosis-damaged enamel surface significantly reduces the adhesion of the brackets20, 23. The research also indicates that fluoride agents reduce adhesive adherence24, but the data on the effect of remineralizing agents on tensile bond strength is controversial.

The study aimed to evaluate the influence of using remineralizing agents on the tensile bond strength.

The present in vitro study was performed at the Department of Orthodontics and the Laboratory of Mechanical Engineering Faculty. Bioethical approval was obtained from the Lithuanian University of Health Sciences Bioethical Committee (No: BEC-OF-106) and the methods were carried out in accordance with the relevant guidelines. Informed consent was obtained from all subjects who participated in the study.

The power analysis with G*Power (Version 3.1.9.2)25 statistical software was used to determine the sample size. The parameters adopted were as follows: significance level of 5%, power test of 80%, the standard deviation of 3, and smallest effect of interest of 2. The calculation of the sample size was based on the following formula:

where n—the minimum sample size for each sample; Z(α/2) = 1.96 and Z(β) = 0.84 if α = 0.05 and β = 0.2; σ—standard deviation; Δ—the smallest clinically important difference.

The sample size calculation showed that at least 18 specimens were needed in each group.

Over a period of 1 month, 80 extracted unhealthy and incurable human molars were collected, remnants of blood and soft tissues were removed, and the teeth were washed under a stream of distillated water. Only the molars with intact enamel surface were used for the study: no decay, no restorations, no cracks from the tooth extraction forceps and no hypoplastic areas. Before the study, the teeth were kept in saline, changing it daily.

The teeth were randomly divided into 4 experimental groups (n = 20): two groups (hereinafter referred to as Fluoride Groups FG1 and FG30), which used chemically cured fluoride varnish (Bifluoride 10, VOCO GmbH, Cuxhaven, Germany), and another two groups (hereinafter referred to as Recaldent Groups RG1 and RG30), which used tooth mousse with bioactive calcium and phosphates (GC Tooth Mousse, GC Europe, Leuven, Belgium). In groups FG1 and RG1, brackets were bonded 1 day after the application of remineralizing agents, and in groups FG30 and RG30—30 days after application. The buccal surface of each tooth was divided into experimental (mesiobuccal) and control (distobuccal) (n = 80). As a result, 160 surfaces were used for the investigation. The brackets of the control group (distobuccal surfaces) were bonded and submitted to a tension test before applying the remineralizing agents to avoid contamination by them.

Before starting testing tensile bond strength, the buccal surface of each tooth was evaluated with a stereomicroscope (Stemi 2000-CS, Zeiss, Oberkochen, Germany) to assess the enamel cracks. The adhesive remnant index (ARI) was also evaluated after the brackets were debonded.

Remineralizing agents were applied according to the manufacturer's instructions. The proximal buccal surfaces of each group (experimental group) were polished with a rubber cup and non-fluoridated pumice, rinsed with distillated water and dried with a stream of air. The experimental surface (mesiobuccal) of the Recaldent tooth mousse groups (RG1 and RG30) was coated with Recaldent tooth mousse (GC Tooth Mousse, GC Europe, Leuven, Belgium) using a micro brush and left for 5 min according to the manufacturer's instructions, then rinsed with distilled water. The procedure was repeated every 6 h within the period of 5 days. Fluoride varnish (Bifluorid 10, VOCO GmbH, Cuxhaven, Germany) was applied on the mesiobuccal surfaces of the groups FG1 and FG30 according to the same protocol as in Recaldent tooth mousse groups26.

Then brackets from the first fluoride varnish group (FG1) and the first Recaldent group (RG1) were bonded and submitted to a tension test 1 day after application (T1). The teeth of the other two experimental groups (FG30 and RG30) were immersed in saline for 30 days (T2), changing it daily, and only then were brackets bonded and the teeth submitted to a tension test19.

Before the bonding procedure, the buccal surface of each tooth was polished with a rubber cup and non-fluoridated pumice, rinsed with water and air-dried. Following, the prepared enamel areas were etched with 37% phosphoric acid gel (i-GEL, i-dental Lietuva, Šiauliai, Lithuania) for 30 s, then washed and air-dried for 20 s until the surface appeared frosted. The etched buccal surface was coated with a thin layer of TruLock bond (Rocky Mountain Orthodontics, Denver, USA) and light-cured for 10 s (3 M ESPE Epilar, Neuss, Germany,1200 mW/cm2).

Directly afterwards, identical premolar metal braces (022 Roth, Discovery, Dentaurum, Ispringen, Germany) were bonded using light-cured TruLock adhesive resin (Rocky Mountain Orthodontics, Denver, USA). Each bracket was positioned 1 mm gingivally to the buccal cusp tip and pressed against the buccal tooth surface with an adapter using a force of 100 g (9.8 N), all done by the same person to ensure the standard thickness of the adhesive. A dental probe was used to remove residual adhesive around the bracket. Bracket adhesive was light-cured for 20 s (3 M ESPE Epilar, Neuss, Germany, 1200 mW/cm2)27, 28. All samples were kept in saline for 24 h after bonding to achieve complete resin polymerization.

The tensile bond strength (TBS) was measured in the Department of Mechanical Engineering at the Kaunas University of Technology. The loops were bent from the orthodontic archwire and fixed to the brackets with ligatures (Fig. 1)20. Then they were adjusted to the universal mechanical testing machine (H24KT, Tinius Olsen, England). The testing machine was used at a crosshead speed of 5 mm/min until the bracket was debonded from the tooth. The highest debonding forces (N) of the brackets were recorded automatically by a digital software measurement system. The system consisted of a force sensor (SS50, Wagner Instruments, USA, 250 N × 0.1 N) and a controller with a display (BGI, Wagner Instruments, USA). TBS was calculated using the force’s value and the base of the bracket area value (1 MPa = 1 N/mm2)20.

Tooth fixed in universal testing machine.

After debonding the brackets, each bracket was analyzed with a stereomicroscope (Stemi 2000-CS, Zeiss, Oberkochen, Germany), and images were taken with a digital microscope camera (AxioCam, MRC 5, Zeiss, Oberkochen, Germany), which were superimposed on a 100 × 100 cell scale20. Adhesive residues were evaluated using the ARI index. The ARI values were divided into 6 groups according to the percentage of adhesive remnant on the bracket: 1—when there is no composite on the bracket base, 2—less than 20% of the composite remains on the bracket base, 3—composite residue covers 20–40% of the bracket base, 4—composite residue covers 41–60% of the bracket base; 5—composite residues cover 61–80% of the bracket base; 6—composite residues cover 81% or more of the bracket base20, 27.

Statistical analysis was performed using IBM SPSS 28.0.1.1. Tensile bond strength (TBS) data were analyzed by one-way ANOVA and Tukey posthoc methods of descriptive statistics. ARI data was analyzed by the Chi-Square method. The difference in results between the variables was considered statistically significant if p < 0.05.

The data obtained was normally distributed according to the Shapiro–Wilk test, so one-way ANOVA and Tukey post-hoc tests were used. Descriptive statistics, including mean, standard deviation, maximum and minimum adhesion force values for each group of brackets, are shown in Table 1. The analysis showed that a statistically significant (p < 0.001) difference in the means TBS was found between the fluoride group FG1 (5.47 MPa; SD = 0.91) when the brackets were debonded the day after application, and the control (7.10 MPa; SD = 0.81) and other experimental groups.

When the brackets were debonded 30 days after the application of fluoride varnish (6.66 MPa; SD = 0.82), the tensile bond strength was lower than in the control group, but no statistically significant difference was found (p = 0.215). No significant difference was found between Recaldent tooth mousse application and different debonding times compared to each other and the control group (p > 0.05) (Fig. 2.).

Average TBS of brackets compared by the different agents used. FG1—fluoride varnish group a day after application; FG30—fluoride varnish group 30 after application; RG1—Recaldent tooth mousse group a day after application, RG30—Recaldent tooth mousse group 30 days after application.

Table 2 shows the adhesive remnant index values. The Chi-Square test showed a statistically significantly higher amount of adhesive residue on the bracket of the FG1 group (p < 0.001) compared to the control group. No statistically significant difference in ARI was found between the other experimental groups and the control group.

The development of caries before and during orthodontic treatment is a significant issue. Prevention of caries and orthodontic treatment are inevitable due to the high prevalence of caries and occlusal anomalies, which rank first and third in all oral diseases, respectively16. However, the influence on TBS of preventive measures of caries that include remineralizing agents is controversial.

In this study, the mean TBS for all groups fell within the Reynolds recommended range of optimal bracket adhesion equal to 5.9–7.8 MPa18 except for the fluoride varnish group, in which the brackets were bonded one day after fluoride varnish application (5.47 MPa; SD = 0.91).

Based on the results obtained and studies performed by other researchers, it can be assumed that the prophylactic use of fluoride leads to lower bracket retention. This is consistent with studies by Leódido et al., Daneshkazemi et al., Cossellu et al., in which the TBS ranged from 6.62 to 9.97 MPa in the fluoride group and from 12.82 to 17.38 MPa in the control group19, 23, 26. This may be since fluoride ions replace calcium ions in the surface layer of the enamel to form fluorapatites, which are more resistant to environmental influences, as well as phosphoric acid, which is used to etch the enamel. As a result, the depth of penetration of the bonding system into the enamel may decrease26. However, such a potential negative effect of fluoride on tensile bond strength should not outweigh its positive effects on prophylaxis.

When evaluating the effect of Recaldent tooth cream, the TBS was lower immediately after application of the cream (6.80 MPa; SD = 0.86) when compared to the control group (7.10 MPa; SD = 0.81) but this difference was not statistically significant (p > 0.05). Cehreli and co-authors as well as Dunne W.J. found that application of CPP-ACP prior to bonding reduced retention28, 29. Naseh et al.30 and Daneshkazemi et al.26 investigated that the use of CPP-ACP cream before fixation of the braces did increase the TBS compared to the control group, although not statistically significant. On the other hand, in studies by Xiaojun et al.31 and Kecik et al.32, this increase was statistically significant. Such different data is possible due to the different methods of application of the substances.

In this study, the application method of remineralizing agents was used as in the study by Daneshkazemi and co-authors26. Both Recaldent cream and fluoride varnish were applied to the tooth surface for 5 min, followed by rinsing with repeated water every 6 h for 5 days. The chosen methodology made it possible to simulate the in vivo study as much as possible but at the same time, to shorten the study time.

However, it is essential to note that in the study, the teeth were kept in saline but not in artificial saliva. According to Naseh and co-authors30, artificial saliva creates the most similar environment to oral conditions. However, in this study, the use of saline was chosen to determine the effect of remineralizing agents alone more objectively on tensile bond strength, ruling out the potential impact of salivary minerals.

Regarding ARI, this study found that a statistically significant amount of resin remained on the bracket in the fluoride varnish group when the brackets were bonded one day after the last application of the fluoride varnish, although in a study by Cossellu and co-authors19 no statistically significant difference was found between ARI values. No significant differences in ARI values between control and experimental groups were found in other studies as well26, 30. However, such results may have been affected by slightly different ARI assessment methodologies and score values19, 21, 26, 30, 32.

Finally, this study showed that remineralizing agents used to prevent caries have a few adverse effects on bracket adherence. That is especially pronounced in the first days after fluoride varnish applications, and the differences become insignificant after 30 days. GC Tooth Mousse Recaldent applications, meanwhile, have a significantly smaller impact. However, for even more accurate results, it would be appropriate to investigate an even larger sample in the future.

This study was an in vitro study, thus it was impossible to repeat the tension test with the same teeth.

Application of fluoride immediately before the bracket bonding procedure significantly reduced tensile bond strength, but after 30 days it was set back to an optimal value.

Application of fluoride immediately before the bracket bonding procedure resulted in the bond failure pattern and a significantly higher ARI score.

Application of CPP-ACP before the bracket bonding procedure had no adverse effect on tensile bond strength.

Application of CPP-ACP had no effect on the bond failure pattern and the ARI score.

A data can be available under reasonable request. If someone wants to request the data from this study a corresponding author Giedrė Trakinienė should be contacted; E-mail [email protected].

Twetman, S. Prevention of dental caries as a non-communicable disease. Eur. J. Oral Sci. 126(Suppl 1), 19–25. https://doi.org/10.1111/eos.12528 (2018).

Article Google Scholar

Peres, M. A. et al. Oral diseases: A global public health challenge. Lancet 394, 249–260. https://doi.org/10.1016/S0140-6736(19)31146-8 (2019).

Article Google Scholar

Wang, Y. et al. Effect of non-fluoride agents on the prevention of dental caries in primary dentition: A systematic review. PLoS ONE 12, e0182221. https://doi.org/10.1371/journal.pone.0182221 (2017).

Article CAS Google Scholar

Lale, S., Solak, H., Hınçal, E. & Vahdettin, L. In vitro comparison of fluoride, magnesium, and calcium phosphate materials on prevention of White Spot lesions around orthodontic brackets. Biomed Res. Int. 2020, 1989817. https://doi.org/10.1155/2020/1989817 (2020).

Article CAS Google Scholar

Hu, H. et al. Effectiveness of remineralising agents in prevention and treatment of orthodontically induced white spot lesions: A protocol for a systematic review incorporating network meta-analysis. Syst. Rev. 8, 339. https://doi.org/10.1186/s13643-019-1253-8 (2019).

Article Google Scholar

Cross, K. J., Huq, N. L., Stanton, D. P., Sum, M. & Reynolds, E. C. NMR studies of a novel calcium, phosphate and fluoride delivery vehicle-alpha(S1)-casein(59–79) by stabilized amorphous calcium fluoride phosphate nanocomplexes. Biomaterials 25, 5061–5069. https://doi.org/10.1016/j.biomaterials.2004.01.045 (2004).

Article CAS Google Scholar

Iijima, Y. et al. Acid resistance of enamel subsurface lesions remineralized by a sugar-free chewing gum containing casein phosphopeptide-amorphous calcium phosphate. Caries Res. 38, 551–556. https://doi.org/10.1159/000080585 (2004).

Article CAS Google Scholar

Khoroushi, M. & Kachuie, M. Prevention and treatment of White Spot lesions in orthodontic patients. Contemp. Clin. Dent. 8, 11–19. https://doi.org/10.4103/ccd.ccd_216_17 (2017).

Article CAS Google Scholar

Thierens, L. A. M. et al. The in vitro remineralizing effect of CPP-ACP and CPP-ACPF after 6 and 12 weeks on initial caries lesion. J. Appl. Oral Sci. 27, e20180589. https://doi.org/10.1590/1678-7757-2018-0589 (2019).

Article CAS Google Scholar

Veena, R. L. & Nagarathna, C. Correlation of streptococcus mutans and streptococcus sobrinus colonization with and without caries experience in preschool children. Indian J. Dent. Res. 31, 73–79. https://doi.org/10.4103/ijdr.IJDR_432_18 (2020).

Article CAS Google Scholar

Attiguppe, P., Malik, N., Ballal, S. & Naik, S. V. CPP-ACP and fluoride: A synergism to combat caries. Int. J. Clin. Pediatr. Dent. 12, 120–125. https://doi.org/10.5005/jp-journals-10005-1608 (2019).

Article Google Scholar

Baysal, A. & Uysal, T. Do enamel microabrasion and casein phosphopeptide-amorphous calcium phosphate affect shear bond strength of orthodontic brackets bonded to a demineralized enamel surface? Angle Orthod. 82, 36–41. https://doi.org/10.2319/041211-265.1 (2012).

Article Google Scholar

Tao, S. et al. Efficacy of fluorides and CPP-ACP vs fluorides monotherapy on early caries lesions: A systematic review and meta-analysis. PLoS ONE 13, e0196660. https://doi.org/10.1371/journal.pone.0196660 (2018).

Article CAS Google Scholar

Ciuffolo, F. et al. Prevalence and distribution by gender of occlusal characteristics in a sample of Italian secondary school students: A cross-sectional study. Eur. J. Orthod. 27, 601–606. https://doi.org/10.1093/ejo/cji043 (2005).

Article Google Scholar

Keski-Nisula, K., Lehto, R., Lusa, V., Keski-Nisula, L. & Varrela, J. Occurrence of malocclusion and need of orthodontic treatment in early mixed dentition. Am. J. Orthod. Dentofacial Orthop. 124, 631–638. https://doi.org/10.1016/j.ajodo.2003.02.001 (2003).

Article Google Scholar

Lombardo, G. et al. Worldwide prevalence of malocclusion in the different stages of dentition: A systematic review and meta-analysis. Eur. J. Paediatr. Dent. 21, 115–122. https://doi.org/10.23804/ejpd.2020.21.02.05 (2020).

Article CAS Google Scholar

Liausas, R., Labanauskas, Z., Svalkauskiene, V., Smailiene, D. & Vaiciuniene, J. Orthodontic treatment complexity, outcome and need among school age patients of Lithuanian university of health sciences clinic of orthodontics. Stomatologija. 21, 28–32 (2019).

Google Scholar

Reynolds, I. R. A review of direct orthodontic bonding. Br. J. Orthod. 2, 171–178. https://doi.org/10.1080/0301228x.1975.11743666 (1975).

Article Google Scholar

Cossellu, G. et al. Timing considerations on the shear bond strength of orthodontic brackets after topical fluoride varnish applications. J. Orthod. Sci. 6, 11–15. https://doi.org/10.4103/2278-0203.197392 (2017).

Article Google Scholar

Trakinienė, G. et al. Impact of fluorosis on the tensile bond strength of metal brackets and the prevalence of enamel microcracks. Sci. Rep. 9, 5957. https://doi.org/10.1038/s41598-019-42325-4 (2019).

Article ADS CAS Google Scholar

Ladhe, K. A., Sastri, M. R., Madaan, J. B. & Vakil, K. K. Effect of remineralizing agents on bond strength of orthodontic brackets: An in vitro study. Prog. Orthod. 15, 28. https://doi.org/10.1186/s40510-014-0028-y (2014).

Article Google Scholar

Trakiniene, G. et al. The effect of the teeth bleaching with 35% hydrogen peroxide on the tensile bond strength of metal brackets. Sci. Rep. https://doi.org/10.1038/s41598-017-00843-z (2017).

Article Google Scholar

da Rocha Leódido, G. et al. Effect of fluoride solutions on the shear bond strength of orthodontic brackets. Braz. Dent. J. 23, 698–702. https://doi.org/10.1590/s0103-64402012000600012 (2012).

Article Google Scholar

Fröhlich, T. T., de Oliveria Rocha, R. & Botton, G. Does previous application of silver diammine fluoride influence the bond strength of glass ionomer cement and adhesive systems to dentin? Systematic review and meta-analysis. Int. J. Paediatr. Dent. 30, 85–95. https://doi.org/10.1111/ipd.12571 (2020).

Article Google Scholar

Faul, F., Erdfelder, E., Buchner, A. & Lang, A. G. Statistical power analyses using G*Power 3.1: Tests for correlation and regression analyses. Behav. Res. Methods 41, 1149–1160. https://doi.org/10.3758/BRM.41.4.1149 (2009).

Article Google Scholar

Daneshkazemi, P., Sadeghian, S. & Khodaei, M. Shear bond strength of orthodontic brackets on intact and demineralized enamel after application of resin infiltrant, fluoride varnish and casein phosphopeptide-amorphous calcium phosphate remineralizing agents: In-vitro study. Int. Orthod. 19, 259–268. https://doi.org/10.1016/j.ortho.2021.03.001 (2021).

Article Google Scholar

Gulec, A. & Goymen, M. Assessment of the resin infiltration and CPP-ACP applications before orthodontic brackets bonding. Dent. Mater. J. 38, 854–860. https://doi.org/10.4012/dmj.2019-021 (2019).

Article CAS Google Scholar

Cehreli, S. B., Sar, C., Polat-Özsoy, O., Unver, B. & Ozsoy, S. Effects of a fluoride-containing casein phosphopeptide-amorphous calcium phosphate complex on the shear bond strength of orthodontic brackets. Eur. J. Orthod. 34, 193–197. https://doi.org/10.1093/ejo/cjq183 (2012).

Article Google Scholar

Dunn, W. J. Shear bond strength of an amorphous calcium-phosphate-containing orthodontic resin cement. Am. J. Orthod. Dentofacial Orthop. 131, 243–247. https://doi.org/10.1016/j.ajodo.2005.04.046 (2007).

Article Google Scholar

Naseh, R., Fallahzadeh, F., Atai, M., Mortezai, O. & Setayeshrad, R. Casein phosphopeptide- amorphous calcium phosphate effects on brackets shear bond strength and enamel damage. J. Clin. Exp. Dent. 9, e1002–e1007. https://doi.org/10.4317/jced.54017 (2017).

Article Google Scholar

Xiaojun, D. et al. Effects of CPP-ACP paste on the shear bond strength of orthodontic brackets. Angle Orthod. 79, 945–950. https://doi.org/10.2319/101108-573.1 (2009).

Article Google Scholar

Keçik, D., Cehreli, S. B., Sar, C. & Unver, B. Effect of acidulated phosphate fluoride and casein phosphopeptide-amorphous calcium phosphate application on shear bond strength of orthodontic brackets. Angle Orthod. 78, 129–133. https://doi.org/10.2319/122506-529.1 (2008).

Article Google Scholar

Download references

We would like to thank Mechanical Engineering faculty Laboratory personae in University of Technology for the opportunity to use their equipment during the investigation.

Department of Orthodontics, Lithuanian University of Health Sciences, Medical Academy, Lukšos –Daumanto 6, Kaunas, Lithuania

Milda Domantaitė & Giedrė Trakinienė

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

M.D. was responsible for the study design, preparation of the materials, analyzed the materials and results, wrote the main manuscript text and prepared it for submission. G.T. was responsible for the study design, for the preparation of the material, analyzed material and results, reviewed the manuscript.

Correspondence to Giedrė Trakinienė.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Domantaitė, M., Trakinienė, G. Influence of the use of remineralizing agents on the tensile bond strength of orthodontic brackets. Sci Rep 13, 507 (2023). https://doi.org/10.1038/s41598-023-27390-0

Download citation

Received: 11 April 2022

Accepted: 02 January 2023

Published: 10 January 2023

DOI: https://doi.org/10.1038/s41598-023-27390-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.